Note: The relative slenderness ratio, Àrel, has been included for information.

5.3.2 Members subjected to compression at an angle to the grain

This is an ultimate limit state condition and using the empirical relationship developed by Hankinson [5] the failure strength of a wood-related product when subjected to a resultant compressive action at an angle a to the grain, fca, as shown in Figure 5.7, can be writtenin terms of its strength parallel to the grain (fc 0) and perpendicular to

Table 5.3 (continued)

Strength class C40 Strength class C45 Strength class C50

E0.05 9400 N/mm2 E0.05 10 000 N/mm2 E0.05 10 700 N/mm2